Abstract
synthesis and characterization of a new chromium- calcium titanate red ceramic pigment is described in this communication. The pigment is based on the solid solution of chromium (IV) in calcium titanate and was characterized as red-brown pigment in a CaO-ZnO-SiO2 transparent glaze used for ceramic tiles (1080°C). XRD, UV-Vis-NIR spectroscopy and CIE-L*a*b* techniques of characterization have been employed. The L*a*b* valour of the optimal pigment with 0,015 mol/mol of chromium fired at 1100°C with a soaking time of 3 hours and 5% weight added to the transparent glaze is 59.3/12.5/9.5. Likewise 5%w. addition of NHCl used as flux agent increase b* and decrease L* valour (L*a*b*=45.2/15.3/5.3).
Publisher
Trans Tech Publications Ltd
Reference11 articles.
1. R.A. Eppler, Black pigments free of heavy metals, US Patent 06/357959, (1983).
2. V. Pishch I and E. V. Radion , Production of white pigments based on zirconates and titanates using the precipitation method , Glass and Ceramics 1998, 55, 9-10.
3. I. V. Pishch I and E. V. Radion , Synthesis of pigments based on perovskite , Glass and Ceramics, 2006, 63(1), 55-58.
4. M. Jansen, H. P. Letschert, Inorganic yellow-red pigments without toxic metals, Nature, 2000, 404, 980-982.
5. G Tobías, Doctoral These, Nuevos oxinitruros laminares de niobio y tántalo y sistemas relacionados, Universitat Autónoma de Barcelona, (2004).
Cited by
13 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献