Abstract
A synthesis study of W2B5 powder was carried out by double self-propagating hightemperature
synthesis (D-SHS) from CaWO4, Mg and B2O3 mixture and followed by HCl leaching
methods. In the first stage of SHS reaction, molar composition ratio of CaWO4:B2O3:Mg mixture
was selected as 1:1:8 (SHS-1) and 1:2.5:8 (SHS-2). The both SHS products were then acid leached
(HCl) at optimum conditions for 1 hour and 80 °C to eliminate MgO, Mg3B2O6 and Ca3(BO3)2
phases. The first leached products were consisted of W, WB, W2B5, and W2B phases. In the second
stage of SHS process, the both leached products were reacted with the same amount of Mg and
B2O3 mixture keeping previous initial ratio values (1:8 and 2.5:8). A successful SHS reaction was
achieved only by using the mixture with leached SHS-2 product. After following acid leaching, the
chemical composition of the leached D-SHS product was found to be 98.2 wt. % W2B5, 1.2 wt. %
WB4, and 0.6 wt. % WB.
Publisher
Trans Tech Publications Ltd
Reference17 articles.
1. S. Stadler, R.P. Winarski, J.M. MacLaren, D.L. Ederer, J. vanEk, , A. Moewes, M.M. Grush, T.A. Callcott and R.C.C. Perera: J. Electron. Spectrosc. 110-111 (2000), pp.75-86.
2. K.A. Khor, L.G. Yu and G. Sundararajan: Thin Solid Films 478 (2005), pp.232-237.
3. M. Stubicar, A. Tonejc and N. Stubicar: Fizika A 4 (1995) 1, pp.65-72.
4. D.L. Perry and S.L. Phillips, Handbook of Inorganic Compounds. CRC press (1995), p.425.
5. H. Kawanowa, Y. Gotoh, S. Otani and R. Souda: Surface Science 433-435 (1999), pp.661-665.
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献