Reactive sintering of elemental powders was used to form Y-doped Mg2Si (Y: 1000, 2000, 3000ppm) using a field-activated pressure assisted synthesis (FAPAS) method. XRD analysis, and the calculation of lattice constant (a) indicates that 1000ppm is the solid solubility of Y in Mg2Si. Sample doped with 2000ppm Y owns better performances, the absolute value of Seebeck Coefficient increases in the temperature of 288-580K and is higher than that of non-doped Mg2Si, and it got higher electric conductivity and higher power factor, which reaches up to 1.67 times of non-doped Mg2Si at 438K and 2.03 times of that of non-doped Mg2Si at about 408K. Meanwhile, the introduction of Y can decrease thermo-conductivity obviously, proving that the introduction of Y is favorable for both electrical and thermal properties.
Publisher
Trans Tech Publications, Ltd.
Reference9 articles.
1. Masayasu Akasaka, Tsutomu Iida, Takashi Nemoto, Junichi Soga, Junichi Sato, Kenichiro Makino, Masataka Fukano, Yoshifumi Takanashi: Journal of Crystal Growth 304 (2007) 196-201.
2. W.J. Luo, M.J. Yang, F. Chen, Q. Shen, H. Y Jiang, and L.M. Zhang: Mater. Sci. Eng. B 157 (2009) 96-100.
3. V.K. Zaitsev, M.I. Fedorov A.T. Burkov, E.A. Gurieva, I.S. Eremin, P.P. Konstantinov, A. Yu. Samunin, S. Sano, S.V. Ordin and M.V. Vedernikov: Proceedings of the 21st International Conference on Thermoelectrics, (2001) pp.151-154.
4. Jun-ichi Tani, Hiroyasu Kido, Intermetallics 15 (2007) 1202e1207.
5. M. Umemoto, Y. Shirai, K. Tsuchiya: Proceedings of the Fourth Pacific Rim International Conference on Advanced Materials and Processing (PRICM4). The Japan Institute of Metals (2001) p.21.
Cited by
11 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献