Abstract
Lead-free 0.85(Bi1/2Na1/2)TiO3- 0.10(Bi1/2K1/2)TiO3- 0.05BaTiO3 (BNKB) ceramics with Li2CO3 or (Bi1/2Li1/2)TiO3 (BLT) added were fabricated by a conventional solid oxide route. The XRD analysis indicates that Li2CO3 introduction leads to the increasing of fraction of tetragonal phase while the BLT introduction does in a reverse tendency. Meanwhile, the depolarization temperature Td of Li2CO3-added BNKB ceramics was enhanced obviously while that of BLT-added BNKB ceramics went down as the addition amount increased. The similarity in variation of the phase structure and the Td of BNKB ceramics reveals the nature of Li+ introduction source on phase structure in BNKB ceramics.
Publisher
Trans Tech Publications, Ltd.
Reference20 articles.
1. G. Smolenskii, V. Isupov, A. Agranovskaya, et al.: Sov. Phys. -Solid State Vol. 2 (1961), p.2651.
2. H. Ishii, H. Nagate, T. Takenaka: Jpn. J. Appl. Phys. Vol. 40 (2001), p.5660.
3. T. Takenaka, K. Maruyama, and K. Sakata: Jpn. J. Appl. Phys. Vol. 30 (1991), p.2236.
4. K. Sakata and Y. Masuda: Ferroelectrics Vol. 7 (19741), p.34.
5. A. Sasaki, T. Chiba, Y. Mamuya, and E. Otsuki: Jpn. J. Appl. Phys. Vol. 38 (1999), p.5564.