The 10NiO-NiFe2O4 composite ceramics doped with NiO were prepared with the cold isostatic pressing-sintering process. The effects of NiO doping order on the density, bending strength and electrical conductivity of NiFe2O4 composite ceramics were studied. The results show that, doping excess 10wt% NiO before synthesis of NiFe2O4 composite (doping order one) and doping excess 10wt% NiO after synthesis of NiFe2O4 composite (doping order two), the former’s samples have a better relative density 88.9% and linear shrinkage rate 9.82%, which is increased by 7.12% and 3.6% compared with that of latter’s samples, respectively. At the same time, the former’s samples also have a better electric conductivity and reach 1.29S/cm at 1233K, which is higher about 13.15% than those latter’s samples. However, the bending strength of the former’s samples just has 76.28Mpa, which is lower about 15.41% than that of the latter’s samples 88.04Mpa.
Publisher
Trans Tech Publications, Ltd.
Reference18 articles.
1. R. P. Pawlek. Inert anodes: an update [A]. Wolfgang Schneider Light Metals 2002[C]. Warreudale PA, USA: TMS, 2002, 449-456.
2. J. D. Weyand, D. H. de Young, S. P. Ray, et al. Inert Anodes for Aluminium Smelting [R]. Washington D C: Aluminum Company of America, February, 1986, 1-516.
3. R. P. Pawlek. Inert anodes for the primary aluminum industry: an update [A]. W. R. Hale, Light Metals 1996[C]. Warreudale PA, USA, TMS, 1996, 243-248.
4. H. B. He, K. C. Zhou, Z. Y. Li, et al. Effect of BaO addition on electric conductivity of xCu/ NiFe2O4-10NiO cermets[J]. Transactions of Nonferrous Metals Society of China, 2008, 18(5): 1134-1138.
5. J. Keniry. The economics of inert anodes and wettable cathodes for aluminum reduction cells [J]. JOM, 2001, 53(5): 43-47.