Considerations on the Ultimate Tensile Strength of Butt Welds of the EN AW 5754 Aluminium Alloy, Made by Friction Stir Welding (FSW)

Abstract

Experiments have been performed for the butt welding of 160 mm x 90 mm x 2 mm sheets of EN AW 5754 aluminium alloy, where the friction stir welding (FSW) has been used.Referring to the parent metal, the chemical composition and the form of wrought products of the aluminium alloy EN AW 5754 is presented, according to the standard EN 573-1:2005, respectively EN 573-3:2013. The mechanical properties of EN AW-5754 (Al Mg3) sheets are presented, according to EN 485-2:2016. The experiments have been conducted on the own equipment for friction stir welding, type FSW-4kW-10kN, to execute 8 (eight) FSW test pieces, according to EN ISO 25239-4. A quenched FSW tool, own-made of C 45 grade steel, EN 10083, has been used. The parameters of the FSW tests are shown. As main parameters, the rotational speed of the FSW tool was in the range n = 800 – 1200 rev/min, respectively the travel speed was in the range v = 50 – 200 mm/min. The run of the joining experiments is described and the joining test pieces are presented in figures. The ultimate tensile strength of the parent metal (σmin,pm) is based on the specified minimum tensile strength of the ”O” condition of the parent material, respectively this value is also required for the weld, that is σmin,w = 190 MPa. The specimens T1.0, T1.1, T2.1, T2.2, T3.1, T3.2, T4.1, T4.2, T5.1, T5.2 și T6.1 are adequate and accepted by this tensile test. The specimens T1.2, T6.2, T7.1, T72. and T8.1 can be accepted, if higher properties are achieved with a full postweld treatment. Another possibility is a lower extent of the minimum tensile strength of the weld that shall be in accordance with another design specification, for example σmin,w = 145 MPa. By the correlation of the FSW parameters with the results of the tensile test, the ranges for the main parameters with adequate values of the ultimate tensile strength are established: n = 800 – 1000 rev/min and v = 50 – 100 mm/min. By the conclusions, the main aspects of the execution of the FSW test pieces, as well as the results of the tensile tests are selected. The involved industrial areas of the applications are: electro-technique, electronics, manufacturing, shipbuilding and automotive industries. The FSW process is ecological, because it neither uses, nor produces hazardous substances. The references consist of 12 titles.