Effect of Electro Deposition Parameters on Thickness and Fe Contents of Nickel-Iron Foam Alloys

Author:

Huo Xiao Min1,He Gang2,Lin Hong Yun3,Wang Jian Li3,Wang De Qing1

Affiliation:

1. Dalian Jiaotong University

2. Fine Chemical Factory of Jilin Petrochemical Co. Ltd

3. Dalian Institute of Product Quality Supervision and Inspection

Abstract

An Ni-Fe alloy on the surface of nickel foam was prepared by electro deposition. The effects of technological parameters including current density, pH value, temperature and the ratio of [Ni2+] to [Fe2+] of planting solution on the thickness and iron content of the alloy coating were studied. The cross-section microstructure and surface morphologies were observed by optical microscopy and scanning electron microscope, and the compositions of the alloy coating were analyzed by energy dispersive spectrometer and ICP-AES. Experiment results show that the thickness of the alloy coating is increased with increasing current density, temperature, pH value and the ratio of [Ni2+] to [Fe2+] of the planting solution. The Fe contents of the alloy coating is increased with increasing current density and pH value of the planting solution, and decreased with increasing temperature and the ratio of [Ni2+] to [Fe2+] of the planting solution. A 36.2 μm thick alloy layer of uniform and dense coating with the Fe content of 60.5 wt% is obtained under the parameters ofn(Ni2+)/n(Fe2+)= 4, current density = 10 A/dm2and pH = 4.2 at 50 °C for one hour.

Publisher

Trans Tech Publications, Ltd.

Subject

General Engineering

Reference22 articles.

1. T. H. Wei, C. Z. Zhang, Z. F. Ping. Technologies and parameters of nickel foam [J]. Chinese Battery Industry. 6(2002): 315-318.

2. Isao Maatsumoto, et al. USP: 4251603, (1981).

3. M. Y. Feng, M. L. Jun, C. Z. Xia. A study absorption property of foamed nickel [J]. Noise and Vibration Control. 2(2001): 13, 30-33.

4. Z. S. Jie. Research on the preparation technology for hydrogen-storage electrode with foam substrate [J]. Chinese Journal of Power Sources. 1(1994): 14-15, 38.

5. S. Gang, C. Chao, P. Fang, et al. Electrodeposition of Ni and Fe alloy on diamond grains [J]. Surface Technology. 36(2007): 49-51.

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3