Abstract
Composition segregation and microstructure nonuniform of H13 steel have been obviously improved though adding nitrogen element. The microstructure and property of H13 steel with nitrogen contents of 0, 0.021%, 0.058% and 0.085% are studied under various quenching and tempering states. Dual quenching that is quenching between 1000~1010°C twice is employed in order to increase the tensile strength and hardness of coupons. The temperature and time are explored for improving the toughness under optimal quenching treatment. For extruding die steel, the tensile strength can reach a satisfactory level and impact toughness are met the requirements of NADCA at the temperature.
Publisher
Trans Tech Publications, Ltd.
Reference7 articles.
1. Mi-Lan Zhang. Abnormal Failure Analysis of H13 Punches in Steel Squeeze Casting process. ISIJ International. (2009), p.421: 424.
2. Basso R.L.O. Influence of microstructure on the corrosion behavior of nitrocarburized AISI H13 tool steel obtained by pulsed DC plasma. Surface and Coatings Technology. (2009).
3. Casteletti L.C. Plasma nitriding of AISI H13 tool steel with different microstructures. ASM International-24th Heat Treating Society Conference (2007).
4. Tong-he, Zhang. Annealing behaviour of H13 steel implanted with N, Ti and Ti+N. Surface and Coatings Technology. (1993).
5. CHEN Jie. The Study of H13 Steel and Its Heat Treatment. Heat treatment Technology and Equipment. 4, 29 (2008)(in chinese).