Microstructure Evolution Behavior of 22MnB5 Pickling Plate during Double Cold Reduction and Rapid Heating Process-Reference-Cited by-同舟云学术

Microstructure Evolution Behavior of 22MnB5 Pickling Plate during Double Cold Reduction and Rapid Heating Process

Published:2014-12 Issue: Volume:1063 Page:47-54
ISSN:1662-8985
Container-title:Advanced Materials Research
language:
Short-container-title:AMR

Author:

Yao Sheng Jie¹,Sun Lei¹,Zhu Hai Hui¹,Wang Guo Dong²

Affiliation:

1. Harbin Institute of Technology at Weihai

2. Northeastern University

Abstract

The microstructure evolution during rapid induction heating process of 22MnB5 steel after double cold rolling was investigated, and the effects of deformation, heating temperature and heating rate on austenitic grain size and micro-hardness of quenched samples were discussed. The results show that the austenite begins to when heated to 850 °C and the austenite grains grow significantly when heated to 950 °C during rapid induction heating process. With the deformation increasing, the austenite grain size decreases, and the austenite grain refinement weakened when the deformation increases to a certain extent; but the influence of cold rolling on micro-hardness after quenching is not significant. In addition, there is little effect of heating rate on the 22MnB5 steel austenite with large cold deformation and a certain effect on the micro-hardness after quenching.

Publisher

Trans Tech Publications, Ltd.

Subject

General Engineering

Link

https://www.scientific.net/AMR.1063.47.pdf

Reference11 articles.

1. LU Chun-yan. Current Status and Development of Automobile lightweight technology [J]. Shanghai Auto, 2007(6): 22-25.

2. LIN Jian-ping, WANG Li-yin , TIAN Hao-bm. Research and Progress of Hot Stamping of Ultrahigh Strength Steel [J]. Material & Heat Treatment, 2008, 37(21): 140-144.

3. HOU, HongmiaoYING, Liang WU, Xiufeng el. at . The influence of heating temperature on 22MnB5 microstructure and austenite grain [J]. China Metalforming Equipment & Manufacturing Technology, 2012, 47(6): 89-91.

4. J Lechler, M Merklein. Hot stamping of ultra high strength steels as a key technology for lightweight construction [A]. In Materials Science and Technology Conference and Exhibition, MS and T'08, October 5, 2008-October 9, 2008[C], 2008: 1698-1709.

5. SUN Cai-na , ZhANG Mei , SHAO Gua-jie el at. Investigation on microstructural evolution of high strength steel 22MnB5 during heating processes [J]. Shanghai metals , 2013 (2): 12-16.