Abstract
The liquidus temperature in the [NaF-AlF3(30 mol.%)]-Sc2O3 molten system with the Sc2O3 additions up to 12 wt% was measured by the thermo analysis. The effect of the cathode current density (0, 0.25, 0.50, and 1.0 A∙cm-2), the Sc2O3 content (1, 2, 4, and 8 wt%) in the NaF-AlF3(30 mol.%)-Al2O3-Sc2O3 electrolyte, the rate of the molten aluminum agitation (0, 100 rotates/min), the synthesis duration (30-210 min) on the Sc content in the aluminum alloy at 980 °С was studied. The Al-Sc alloys with the scandium content of 0.15-1.30 wt%, depending on the synthesis conditions, and with the uniform Sc distribution throughout the aluminum matrix were produced.
Publisher
Trans Tech Publications, Ltd.
Reference4 articles.
1. J. Royset, N. Ryum, Scandium in aluminium alloys, Int. Materials Reviews 50 (2005) 19-44.
2. V.I. Moskvitin, S.V. Makhov, On possibility of fabrication of aluminum-scandium alloying composition in aluminum electrolyzer, Tsvetnye Metally (Russian Journal of Light Metals), 1998, №7, 43-46.
3. Y. Qian, J. Xue, Q. Liu, J. Zhu, Preparing Al-Sc-Zr alloys in aluminum electrolysis process, Light Metals (2013) 1311-1314.
4. Q. Liu, J. Xue, J. Zhu, Ch. Guan, Preparing aluminium-scandium inter-alloys during reduction process in KF-AlF3-Sc2O3 melts, Light metals (2012) 685-689.
Cited by
6 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献