Abstract
In order to improve the water resistance of silicate wood adhesive, a kind of silicate adhesive was prepared from water glass with silica as curing agent, and ammonium stearate as modifier. The chemical structure, surface morphology and thermal properties of the silicate adhesive were characterized by Fourier transform infrared spectrometer, scanning electron microscope, and thermo-gravimetric analyzer. As the two main measures of adhesion properties, the bonding strength and water resistance were also determined. The results showed that ammonium stearate was successfully introduced into the molecule structure of silicate, the silicate adhesive have good thermal stability in the range of 30~800 °C and the modified silicate adhesive had more smooth cured morphology. The bonding strength and 24h water absorption rate of poplar plywood glued by the silicate adhesive was 0.71 MPa and 22.81%, respectively, reaching the grade II of plywood performance's national standard.
Publisher
Trans Tech Publications, Ltd.
Reference16 articles.
1. Qin Zhang, Shouzhi Yi and Hongyun Ma: China Adhesives (in Chinese), Vol. 20 (2011), p.41.
2. V.A. Voitovich: Polymer Series D—Glues and Sealing Materials, Vol. 2 (2009), p.187.
3. CanShan Jiao, Zhengping Wang and Weijun Zhang: Chemical and Adhesion (in Chinese), Vol. 4 (1999), p.203.
4. S.S. Kouassi, M.T. Tognonvi and J. Soro: Journal of Non-Crystalline Solids, Vol. 357 (2011), p.3013.
5. XianGuang Zeng, Xinyue Li and QiaofengYang: Electroplating & Finishing (in Chinese), Vol. 29 (2010), p.51.
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献