Abstract
To overcome the disadvantage of MgO-CaO refractories, as the poor hydration resistance, MgO coating on the MgO-CaO clinker was fabricated by carbothermal reduction MgO with carbon as reduction agent and then the oxidation of Mg vapor. Effect of processing parameters (such as carbon source, reaction temperature and holding time) on the hydration resistance of MgO-CaO clinkers were investigated by hydration resistance test and SEM. The results indicated that the hydration resistance of treated MgO-CaO clinkers was improved when carbon black was used as reduction agent due to easy reaction with MgO than the graphite and coke. The high reaction temperature among 1450~1600°C and prolonged holding time within 4 h resulted in improvement of the hydration resistance of treated MgO-CaO clinker. Deposition mechanism of MgO coating on the MgO-CaO clinker was discussed.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference6 articles.
1. Shujiang Chen and Pingge Lu: J. Am. Ceram. Soc. Vol. 87 (2004), p.2164.
2. Yanlong Ma, Hongfeng Yin, Xubo Shi, Kedi Shou: Naihuocailiao, Vol. 44(3) (2010), p.192.
3. Min Chen, Caiyun Lu, Jingkun Yu: J. Europ. Ceram. Soc. Vol. 27 (2007), p.4633.
4. Z. Li, S. Zhang and W. E. Lee: International Materials Reviews, Vol. 53(1) (2008), p.1.
5. Guoqing Xiao and Xinghua Yang: Naihuocailiao, Vol. 32(2) (2008), p.77.
Cited by
16 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献