The Ba5(Nb1-xTax)4O15 (x=0~0.5) solid-solution ceramics with hexagonal perovskite structure were prepared by solid-state oxide route. The phases and structure of the sintered ceramics were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The influences of composition and sintering temperature on the bulk density, microstructure and microwave dielectric
properties were also investigated. As the value of x increased from 0 to 0.5, the Q×f value increases from 36,049 to 49,493 GHz (at ~9GHz), whereas the dielectric constant (εr) decreases from 39.21 to 33.03 and the temperature coefficient of resonant frequency (τf ) decreases from 78.6 to 19.4 ppm/oC. The results
indicate that the microwave dielectric properties of Ba5(Nb1-xTax)4O15 ceramics can be easily modified in a large range by changing the relative content of Ta to Nb.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference8 articles.
1. D. Cruickshank: J. European Ceram. Soc. Vol. 23 (2003), p.2721.
2. F. Galasso and L. Katz: Acta Crystallogr. Vol. 14 (1961), p.647.
3. N.E. Massa, S. Pagola and R.E. Carbonio: Phys. Rev. B. Vol. 53 (1996), p.8148.
4. N.E. Massa, S. Pagola, R.E. Carbonio, J.A. Alonso, I. Rasines, G. Polla and G. Leyva: SPIE International symposium, San Jose, CA, USA.
5. S. Kamba, J. Petzelt, E. Buixaderas, D. Haubrich and P. Vaněk: J. Appl. Phys. Vol. 89 (2001), p.3900.
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献