Evaluation of the Material Properties of the Ti and CoCr Alloys Prepared by Laser Powder Bed Fusion

Abstract

The main aim of the present paper is evaluated the mechanical properties, microstructures and porosity of Ti6Al4V and CoCrW alloys produced by Laser Powder Bed Fusion (L-PBF) as an additive manufacturing (AM) technology. The mechanical properties were follows: For Ti6Al4V alloy the UTS was 1180 MPa; the YS was in the range <600; 745 MPa>. For CoCrW alloys, the UTS were in range <750; 950 MPa> and YS was in range <400; 500>. Evaluation of porosity was realized on non-etched samples using by quantitative image analysis in order to describe the dimensional and morphological porosity characteristics. The pores in the Ti6Al4V alloy showed homogeneous distribution without significant large pores.