New Materials for Semi-Insulating SiC Single Crystal Growth by PVT Method

Abstract

The present research was focused on the effect of porous graphite plate in TaC-coated crucible on crystal quality and resistivity of semi-insulating SiC crystals. Two SiC crystals grown with/without porous graphite plate in TaC-coated crucible were systematically compared. 6H-SiC polytype was obtained on both crystals regardless of porous graphite plate. The quality of SiC crystal grown using porous graphite plate placed in the TaC-coated crucible was slightly better than SiC crystal without porous graphite plate. SiC crystals having an average resistivity value of about 1×1010 Ωcm were obtained. In the result of COREMA measurement, the use of porous graphite plate tends to obtain wafers with better uniformity in resistivity value.