Abstract
The influence of time and temperature of ageing on the σ-phase morphology in ferritic-austenitic cast steel have been investigated in this study. The morphology and quantity of the σ-phase were analyzed by using optical microscope, X-ray diffractometry, scanning electron microscope and image analysis, respectively. The annealing temperature has a significant influence on the morphology, volume fraction and the dynamics of σ-phase precipitation. Surface development of the σ-phase decreases from R=4.3, for the cast steel annealed at 700°C to R=2.4 for the cast steel annealed at 900°C, and the volume fraction Vvσ from 50.8% to 26.5%, respectively. The most rapid progress of δ → σ + γ’ transformation was observed at 800°C.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference15 articles.
1. R. Badji, M. Bouabdallah, B. Bacroix, C. Kahloun, B. Belkessa, H. Maza, Phase transformation and mechanical behaviour in annealed 2205 duplex stainless steel welds, Materials Characterization 59, (2008), 447-453.
2. K. A. Bakken, Cost effective materials selections – what is true?, Stainless Steel World Conference & Expo, Maastricht Netherlands, (2005), pp.18-23.
3. S.K. Ghosh, S. Mondal, High temperature ageing behaviour of a duplex stainless steel, Materials Characterization 59, (2008), 1176-1783.
4. Y-J. Kim, O. Ugurlu, C. Jinag, B. Gleeson, Microstructural evolution of secondary phases in the cast duplex stainless steel CD3MN and CD3MWCuN, Metallurgical and Materials Transactions A, Vol. 38A, (2007), 203-211.
5. H. Sieurin, R. Sandstrom, Sigma phase precipitation in duplex stainless steel 2205, Materials Science and Engineering A 444, (2007), 271-276.
Cited by
10 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献