Tensile Properties of a Low-Cost First Generation Single Crystal Superalloy DD16

Abstract

The tensile properties of a low-cost first generation single crystal superalloy DD16 have been investigated. The results show that values of the tensile strength and yield strength of DD16 alloy were similar at typical temperatures; from room temperature to 760, the yield strength of DD16 alloy increases; However, above 760, the yield strength of DD16 alloy decreases remarkably, and the maximum of the yield strength was 1145.5MPa at 760. From room temperature to 760, the fracture mode was cleavage fracture; But above 760, the fracture characteristics changed from cleavage to dimple.