Abstract
Failure analysis of fracture of 35CrMo bolt was investigated. It was analyzed by means of morphology and microstructure analysis, chemical composition analysis, hydrogen content analysis, scanning electron microscope (SEM) micro-morphology of fracture surface, electronic differential system (EDS) corrosion products analysis. The results showed that the cause of fracture of 35CrMo bolt was stress corrosion cracking. Working stress of the bolt，H2S in surroundings and the high hardness of the bolt combined caused cracking of the bolt. Suitable heat treatment for the 35CrMo bolt is suggested.
Publisher
Trans Tech Publications, Ltd.
Reference9 articles.
1. Ke Wei. Corrosion investigation report in China. Beijing: Chemical Industry Press, 2003: 38.
2. YANG Huai-yu, CHEN Jia-jian, CAO Chu-nan etal. Study on corrosion and inhibition mechanism in H2S aqueous solutions. Journal of Chinese society for corrosion and protection, 2000, 20（2）: 97.
3. Xiao Ji-mei. Metal Corrosion under Stress[M]. Beijing: Chemical Industry Press, 1990: 27.
4. Carneiro RA, Ratnapuil RC, de FREITAS Cunha Lins V. The influence of chemical composition and microstructure of API line steels on hydrogen induced cracking and sulfide stress corrosion cracking[J]. Material science and Engineering. A2003(357): 104~110.
5. Elboujdaini M, Revie RW. Metallurgical factors in stress corrosion cracking(SCC) and hydrogen-induced cracking(HIC)[J]. Electrochemical and Solid State Letters, 2009, 13: 1091~1099.
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献