Hypostoichiometric Fe-Pd binary alloys (35-45 at% Pd) were severely deformed (>90%) and subsequently aged to induce concomitant recrystallization, precipitation, and ordering. This thermomechanical processing strategy was articulated by Hornbogen [1] over thirty years ago. The resulting exchange-coupled ferromagnets contain ferrite precipitates and a complex metastable two-phase lamellar transformation product comprised of ordered L10 and a metastable FCC phase. The later duplex microconstituent is suggested to form in conjunction with a so-called pseudospinodal reaction [2] involving emerging cubic and tetragonal phases, whereby phase separation and ordering result from continuous changes in composition and a reduction in symmetry, cubic to tetragonal. The deformation texture of the parent austenite is substantially retained in the transformation product, resulting in anisotropy of the magnetic properties as determined by magnetometry (VSM). This paper presents electron microscopy results elucidating the crystallography and morphology of the phase mixtures including HREM. Magnetic field annealing is also included as a branch of our thermomechanical processing strategy, and we discuss the influence of the external fields on recrystallization, precipitation, and ordering.
Publisher
Trans Tech Publications, Ltd.
Subject
Condensed Matter Physics,General Materials Science,Atomic and Molecular Physics, and Optics
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献