Zeolite / MC nylon 6 composites were prepared , followed by morphology and properties characterization of composites. The results demonstrated that a large number of pearlitic structures appeared at the interphase between the organic phases and the inorganic phases, indicating that caprolactam had happened anionic in-situ polymerization within the zeolite. The zeolite played a role of molecular rivet in zeolite / MCPA6 composites. The experimental results also showed that the composites performances were largely improved compared with pure MCPA6. When zeolite was 1 Phr, the impact strength of the composite was increased by 58%, temperature of thermal decomposition was rised by 92.9 °C. When zeolite reached 5 Phr, the composite shrinkage rate was reduced by 33%.
Publisher
Trans Tech Publications, Ltd.
Reference4 articles.
1. F.P. La Mantia, L. Capizzi. et al: Polymer Degradation and Stability Vol. 71 (2001), p.285.
2. Dong Weifu, Liu Yiqun, Zhang Xiaohong. et al: Macromolecules Vol. 38 (2005), p.551.
3. Bofen Huang, Hanxuan Liang, Yanchao Bai. et al: Applied Mechanics and Materials Vol. 295-298 (2013), p . 426.
4. Tsai WT: Journal Of Hazardous Materials Vol. 166 (2008), p.635.