Affiliation:
1. Silesian University of Technology
2. Stanislaw Staszic Research Institute of Ferrous Metallurgy
Abstract
Two 5Mn-1.5Al TRIP steels with and without Nb microaddition were developed in the present study. The steels contain bainite, martensite, interlath retained austenite and martensite- austenite islands. The paper presents the results of the compression tests carried out at various temperatures using the Gleeble simulator. To analyze the kinetics of static recrystallization in these steels, a softening kinetics were determined in a double-hit compression test. It was found that the dynamic recovery is a main thermally activated process occurring during hot deformation. The Nb microalloyed steel has higher flow stresses and peak strains than the Nb-free steel. A solute drag effect of Nb results in a slower softening kinetics of Nb containing steel. The effects of Mn on the retardation of Nb(C,N) precipitation and hot deformation characteristics are also discussed.
Publisher
Trans Tech Publications, Ltd.
Reference12 articles.
1. M.J. Merwin: Iron and Steel Technology Vol. 5, No. 10 (2008), pp.66-84.
2. S.J. Kim: Materials Science Forum Vol. 638-642 (2010), pp.3313-3318.
3. B.C. De Cooman, S. Lee and S.S. Kumar: 2nd Inter. Conf. on Super-High Strength Steels (2010), Peschiera del Garda, Italy, pp.1-11.
4. N. Cabanas, N. Akdut, J. Penning and B.C. De Cooman: Metallurgical and Materials Transactions Vol. 37A (2006), pp.3305-3315.
5. A.S. Hamada, L.P. Karjalainen and M.C. Somani: Materials Science and Engineering A Vol. 467 (2007), pp.114-124.
Cited by
26 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献