Affiliation:
1. Changchun University of Science and Technology
Abstract
Laser surface modification, using a continuous wave CO2 crosscurrent laser with generated beam power of 1 kW, was performed on the adamite steel, indefinite chilled cast iron and high speed steel rolls which were applied to the industries. Optical microscopy, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS) and micro Vickers hardness test were applied to reveal the microstructural details and hardness profiles of the laser treated zone. The results indicate that, laser treated zones of three roll samples consist of melting zone, phase transformation zone and heat affected zone. After laser treatment, the melting zone have low hardness compared to the phase transformation zone, but after tempering at 540°C for 1 hr, the hardness at the melting zone dramatically increases, because of the formation of the fresh martensite from retained austenite. In contrast, the hardness at the phase transformation zone sharply decreases as fresh martensite changed to tempered martensite. There are many small and well distributed FeS and MnS inclusions in the melting zone at the three roll samples.
Publisher
Trans Tech Publications, Ltd.
Reference14 articles.
1. Chen C H, Alstetter C J: Metall Trans, Vol. 15A (1984), p.719.
2. Trafford D, Bell N T, Megaw J H: Met Technol., Vol. 13 (1983), p.69.
3. Christodoulou G, Walker A, West D R F, et al.: Met Technol., Vol. 13(1983), p.215.
4. Abboud J H, West D R F: J Mater Sci Lett, Vol. 11 (1992), p.1322.
5. Zhengyang Li, Zhiyi Du, Bingyi Wang et al.: China International Steel Mill Rolls Conference, June 2-4, 2008, China Iron and Steel Association, p.350.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献
1. Introduction;Advanced Topics in Science and Technology in China;2020-12-01