Effect of Carbon Source on Synthesis of Carbon Coated Lithium Titanate

Abstract

Carbon coated lithium titanate (Li4Ti5O12/C) was obtained by a facile solid state approach in inert Ar atmosphere. The composition, morphology, residual carbon content and Ti valence of the samples were systematically investigated. The carbon content of Li4Ti5O12/C should be optimized, since excess carbon in the composite leads to the reduction of Ti (IV) to form Ti (III), which results in large irreversible capacity of Li4Ti5O12/C. With an optimal carbon content of 0.68wt%, the Li4Ti5O12/C sample shows high rate capabilities and good cycling ability, delivering discharge capacities of 160.8 mAh/g at 5C. The superior high rate properties are ascribed to the specific nanostructures, which enables fast electronic and ionic transport by introducing carbon coating and decreasing the particle size of lithium titanate.