Abstract
Melt holding time has important influences on the modification effect of Sr modified AS31 alloy. Effects of different melt holding time (30min, 60min, 90min and 120min) at 700°C on as cast microstructure and tensile properties both at ambient temperature and elevated temperature of Sr-modified AS31 alloy were studied. There exist polyhedral shape, fine fibers shape and a few Chinese script Mg2Si particles in Sr-modified AS31 alloys. And the average grain size is smallest in Sr-modified AS31 alloys with holding time at 700°C for 30min. The ultimate strength, yield strength and elongation at both ambient temperature and 150°C decrease gradually when the melt holding time increases from 30min to 120min. In the process of smelting of Sr-modified AS31. The burning loss of Sr element becomes more serious with the prolongation of melt holding time, which contributes to the modification effect reducing.
Publisher
Trans Tech Publications, Ltd.
Reference13 articles.
1. J.M. Kim, K. Shin, K.T. Kim and W.J. Jung: Scripta Mater Vol. 49 (2003), p.687.
2. Z, Yang, J.P. Li, et al: Acta Metallurgica Sinica Vol. 21 No. 5 (2008), pp.313-328.
3. H. Xu, J.A. Lu, and S.S. Xie: Metallurgical Industry Press, Beijing, 2007: 2.
4. Y.C. Pan, X.F. Liu and H. Yang: Mater Charact Vol. 55 (2005), p.241.
5. S. Barbagallo, P. Cavaliere and E. Cerri: Mater Sci Eng Vol. A367 (2004), p.9.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献