Affiliation:
1. Zhejiang University of Technology
Abstract
The fatigue crack growth tests of compact tension (CT) specimens of 2024-T4 aluminum alloy were conducted under constant amplitude loading with differentR-ratios, 0.05, 0.1, 0.5, 0.75, respectively. The thickness of the specimen is 3.8mm. All the fatigue crack growth experiments were carried out in ambient air without a pre-crack. The early crack growth region reflects the influence of the notch. An optical reading micrometer with a magnification of 40 was used to measure the crack length. The size of the notch together with the loading conditions has a great influence on the early crack growth within the notch influenced region. Beyond the notch influenced zone, the stable fatigue crack growth is reached and can be characterized by the Paris law. The experimental results indicate that fatigue crack growth rate increases with theR-ratio for a given stress intensity factor amplitude.
Publisher
Trans Tech Publications, Ltd.
Reference11 articles.
1. X.G. Wang, Z.L. Gao, B.X. Qiu, L.M. Wang and Y.Y. Jiang: Chin. J. Mech. Eng. DOI: 10. 3901/CJME. (2011).
2. X.G. Wang, Z.L. Gao, T.W. Zhao and Y.Y. Jiang: J. Pressure Vessel Technol. Vol. 5(2009), p.0214021.
3. S. Kalnaus, F. Fan, Y.Y. Jiang and A.K. Vasudevan: Int. J. Fatigue. Vol. 31(2009), p.840.
4. T.W. Zhao, J.X. Zhang and Y.Y. Jiang: Int. J. Fatigue. Vol. 30(2008), p.1169.
5. S. Kalnaus, F. Fan, A.K. Vasudevan and Y.Y. Jiang: Eng. Fract. Mech. Vol. 75(2008), p. (2002).
Cited by
9 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献