AISI H13 Hot-Work Steel with Hard Chromium Plating Thermal Fatigue Behavior Evaluation

Author:

Yeh Shu Hung,Chiu Liu Ho,Lin Shou Chi,Pan Yeong Tsuen

Abstract

A hard-coating on hot work tool steel can be used to obtain higher corrosion resistance, as well as better wear resistance. This study investigates the thermal fatigue performance of AISI H13 hot work tool steel with and without hard chromium plating. Treated specimens were characterized using microstructural analysis, X-ray diffraction analysis and microhardness measurement. The thermal fatigue test is based on cyclic induction heating and water cooling. The specimen was heated to the maximum surface temperature of 670°C followed with water injection to bring the specimen down to a minimum temperature of 25°C. The thermal fatigue testing in this study was conducted using 500 cycles. A vacuum heat treated specimen with a hardness of 47 HRC was used as the reference material. The hard chromium plated layer with a thickness 35 μm had a hardness of 930 HV0.1. The damage factor, defined as crack depth × crack width, of quenched and tempered H13 specimens and hard chromium plated specimens were 800 and 1760, respectively. The damage factor evaluation verified the vacuum heat treated specimen thermal fatigue resistance is superior to that of the hard chromium plated specimen.

Publisher

Trans Tech Publications, Ltd.

Subject

General Engineering

Cited by 1 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3