Abstract
The results of microstructure and phase composition investigations of titanium in different structural states (with average grain sizes of 0.3 μm, 1.5 μm, 17 μm, 38 μm) implanted by Al ions using the «Raduga-5» and MEVVA–V.RU sources are presented. The size, shape and localization of the formed phases (TiO2, Ti2O, TiC, Ti3Al, TiAl, Al3Ti) depend strongly on the grain size of titanium target. In polycrystalline titanium after implantation by Al-ions the secondary phases (Ti3Al, TiAl, TiO2, TiC) formed in the body of grains of titanium matrix. It is shown that the nanostructural particles of TiO2 phase are located mainly on dislocations in the body of target grains. An ordered Ti3Al phase is located at a depth of more than 200 nm in the implanted layer along the boundaries of the titanium grains. The TiAl3 phase formed on the grain boards in subnano- and microstructural state of titanium targets. The improvement of the mechanical properties of titanium due to formation of the gradient structure of ion-alloyed surface layer was obtained.
Publisher
Trans Tech Publications, Ltd.
Reference9 articles.
1. E.V. Kozlov, A.N. Zhdanov, and N.A. Koneva, Deformation mechanisms and mechanical properties of nanomaterials, Physical mesomechanics, 2007, V. 10, № 3, p.95–103.
2. R. A. Andrievskiі and A. M. Glezer, Strength of nanostructures, Physics-Uspekhi, 2009, V. 52, № 4, p.315–334.
3. I.A. Kurzina, E.V. Kozlov, Yu.P. Sarkeev et al., Nanocrstalline intermetallic and nitride structures formed under ion-beam influence Materials, Izdatelsto NTL, Tomsk, 2008 – 325 p. [In Russian].
4. A.N. Didenko, Yu. P. Sharkeev, E.V. Kozlov, and A.I. Ryabchikov, Effects of Long-Range Action in Ion-Implanted Metallic Materials, Izdatelstvo NTL, Tomsk, 2004 – 328 p. [In Russian].
5. I.B. Stepanov, A.I. Ryabchikov, E.V. Kozlov, et al., High-current vacuum-arc ion and plasma source «Raduga-5» application to intermetallic phase formation, Review of scientific instruments, 2006, V. 77, № 3, pp. 03C115-1–03C115-4.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献