Structure and Properties of High-Chromium-Alloyed Upper-Eutectoid Steels after Hardening with Concentrated Energy Fluxes-Reference-Cited by-同舟云学术

Structure and Properties of High-Chromium-Alloyed Upper-Eutectoid Steels after Hardening with Concentrated Energy Fluxes

Published:2009-12 Issue: Volume:83-86 Page:896-903
ISSN:1662-8985
Container-title:Advanced Materials Research
language:
Short-container-title:AMR

Author:

Stavrev Dimitar¹,Dikova Tsanka D.²

Affiliation:

1. Technical University of Varna

2. Medical University of Varna

Abstract

The present paper deals with the structure and properties of two types of tool steels with high chromium content (12% Cr) hardened by means of Concentrated Energy Fluxes (CEF). The treatment conditions are chosen to ensure liquid state transformations. The melted zone of the surface layer features a quasi-ledeburite structure, consisting of inhomogeneous residual austenite and Cr-containing carbides of MmCn type. This austenite is strongly cold hardened and over-saturated with Cr and carbon. The micro-hardness of this region varies from 400 up to 800 HV0.1. The higher the energy density, the lower the hardness and the wider the modified layers. The lower hardness is due to the presence of nearly 100% austenite. Higher hardness was obtained in the heat affected zone. Carbides of M23C6, M7C3, M6C, M3C and МС types were identified. A scheme of carbide changes after treatment with CEF is given.

Publisher

Trans Tech Publications, Ltd.

Subject

General Engineering

Link

https://www.scientific.net/AMR.83-86.896.pdf

Reference16 articles.

1. V.A. Guiva et al., Izvestia VUZ, Chernaia metallurgia, 1980, ʋ11, pp.106-111.

2. H.W. Bergmann, G. Barton, I. Betz, Z. Werkstofftech, 14, 1983, s. 244-252.

3. M.A. Kipnis et al., Tehnologia i organizacia proizvodstva, 1984, ʋ1, p.43.

4. D. Stavrev, S. Kirov, XII Celostatne Dni Tepelneho Spracovania, Bratislava, 1/88, s. 97-99.

5. A.A. Uglov, B.S. Medres, A.A. Solovev, Fizika i himia obrabotki materiallov, ʋ3, 1987, pp.6-10. Ɇ23ɋ6 Ɇ6ɋ L CrFe c , )( Ɇ3ɋ Ɇ23ɋ6 L CrFe c , )( M6C Ɇ3ɋ6 Ɇ6ɋ L CrFe c , )( Ɇ7C3 Ɇ23ɋ6 CrFe c , )( M6C M3C L (8) (9) (10) (11).