Abstract
Fe-doped zinc oxide nanorods (ZnO NRs) were synthesized by ex-situ doping using spray pyrolysis technique. In this work, the undoped ZnO NRs were pre-synthesized via chemical vapor deposition using Zn powder and oxygen gas at 650 °C. The average length and diameter of the ZnO NRs are 4.1 ± 1.1 μm and 553.1 ± 89.6 nm, respectively. The average aspect ratio and areal density of ZnO NRs is 8.2 ± 2.9 and 6.2 ± 1.1 NRs/um2, respectively. Subsequently, these undoped ZnO NRs were kept in the horizontal tube furnace, whereas the dopant solution (FeCl3) of 0.05 M concentration was kept in the aerosol generator, which was located outside of the furnace. The Fe aerosol was flowed into the reactor when substrate temperature reached 650 °C to achieve ex-situ doping. At this temperature, some of the Fe atoms were driven into the NRs, forming Fe-doped ZnO NRs particularly at their outer layer. The presence of Fe 2p1/2 and Fe 2p3/2 peaks at 722.3 eV and 705.7 eV in XPS analysis indicates that Fe atoms were in the local structure of FeO. The Fe-doped ZnO NRs have poor crystal quality attributed to the low IUV/IVis ratio in room temperature PL analysis.
Publisher
Trans Tech Publications, Ltd.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献