Abstract
The microstructures of 30Mn20Al3 non-magnetic steel after different finishing temperature and cooling rates have been studied by multi-pass compression test in a thermal-mechanical simulator. The results show that the microstructure of this steel is totally of austenitic with amounts of twins. At the same cooling rate, larger amount of thicker twins appear when lowering finishing temperature. The austenite grain size is related to finishing temperature and cooling rate. The critical temperature of austenite recrystallization is determined as 950~1000°C. When the finishing temperature is about 1000°C and cooling rate higher than 15°C/s, fine and uniform austenite grains can be obtained.
Publisher
Trans Tech Publications, Ltd.
Reference5 articles.
1. Y. Sh. Zhang, L. J. Su: Acta Metallurgica Sinica, Vol. A19 (1983): p.253. (in Chinese).
2. Y. Sh. Zhang, Ch. X. Shi: Acta Metallurgica Sinica, Vol. 7 (1964): p.285. (in Chinese).
3. X. Tian, Y. Sh. Zhang: Materials Science and Engineering A, Vol. 174 (1994): p. L1.
4. X. Tian, Y. Sh. Zhang: Materials Science and Engineering A, Vol. 56 (2009): p.78.
5. Z. Zh. Yuan, Y. Kuang, X. D. Chen, Sh. Qiu: Materials for Mechanical Engineering, Vol. 29 (2005): p.9. (in Chinese).
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献