Abstract
Hydroxyapatite of calcium phosphate materials, one of the most frequently used ceramic material in biomedical application, has been produced via chemical reaction involves both calcium and phosphorus precursors. Effect of suspension concentration on available phases was investigated using a basis of 2 mole % excess of calcium oxide. The synthesis was performed at 90°C until paste was obtained. To improve crystallinity, hydroxyapatite was calcined at 900°C. However, β-TCP appeared as trace which varied in fraction with suspension concentration. Varying concentration is then one approaching method in designing phase composition through which a functional material could be attained.
Publisher
Trans Tech Publications, Ltd.
Reference13 articles.
1. H. Ye, X.Y. Liu and H. Hong: J. Mater. Sci: Mater. Med. Vol. 20 (2009), p.843.
2. T. Nomoto, K. Haraguchi, S. Yamaguchi, N. Sugano, H. Nakayama, T. Sekino and K. Niihara: J. Mater. Sci: Mater. Med. Vol. 17 (2006), p.379.
3. M.P. Ferraz, F.J. Monteiro and C.M. Manuel: J. App. Biomater. Biomech. Vol. 2 (2004), p.74.
4. H. Kim, R.P. Camata, Y.K. Vohra and W.R. Lacefied: J. Mater. Sci: Mater. Med. Vol. 16 (2005), p.961.
5. B. Li, X. Chen, B. Guo, X. Wang, H. Fan and X. Zhang: Acta Biomaterialia Vol. 5 (2009) p.134.
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献