Abstract
To analysis the microstructure and properties of super-high strength Al-Zn-Mg-Cu alloys containing Zr ,Ni and Mn, the apparatus of SEM、TEM、and Tensile machine was used. The results show that the microstructure was fine and homogeneous, the phases became finer for the alloys with adding Zr, Mn, Ni than the alloy with Zr only after solid solution. The ultimate tensile strength of the alloy was 850MPa and the elongation was 5% respectively at peak aging.
Publisher
Trans Tech Publications, Ltd.
Reference11 articles.
1. Robinson JS, Cudd RL, Tanner DA. Quench sensitivity and tensile property inhomogeneity in 7010 forgings. J Mater Process Technol 2001; 119: 261–7.
2. Liu SD, Zhang XM, Chen MA. Effect of Zr content on quench sensitivity of AlZnMgCu alloys. Trans Nonferrous Met Soc China 2007; 17: 787–92.
3. C. Mondal, A.K. Mukhopadhyay, T. Raghu, and V.K. Varma, Tensile properties of peak aged 7055 aluminum alloy extrusions, Mater. Sci. Eng. A, 455(2007), No. 3, p.673.
4. M. Dixit, R.S. Mishra, and K.K. Sankaran, Structure-property correlations in Al 7050 and Al 7055 high-strength aluminum alloys, Mater. Sci. Eng. A, 478(2008), No. 1-2, p.163.
5. S.D. Liu, X.M. Zhang, M.A. Chen, et al., Influence of aging on quench sensitivity effect of 7055 aluminum alloy, Mater. Charact., 59(2008), No. 1, p.53.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献