The effect of neutron irradiation on superconducting properties of Bi2Sr2CaCu2 (Bi-2212) phase superconductor was studied. TRIGA MARK II research reactor with neutron flux of 2.00 × 1011 /cm2s was used as the neutron source. Results between non-irradiated and irradiated samples have been analyzed from the aspects of microstructure and electrical properties. In this work, the bulk samples were prepared using the conventional solid-state reaction method. Molar ratio of Bi2O3, Sr2CO3, CaCO3 and CuO were mixed according to its ratio into composition of Bi:Sr:Ca:Cu = 2:2:1:2. The samples were sintered at 840°C during the sample preparation process. Some of the fully synthesized samples were irradiated with neutron irradiation. Neutron irradiation has been proved to promote better flux pinning properties by introducing larger defects in various superconductor ceramics. Enhanced flux pinning centers in the superconductor is responsible in enhancing the critical current, Ic and critical current density, Jc of the irradiated samples. The samples were characterized through X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). The transition temperature, Tc and the Jc were measured by using a cryogenic four-point probe system. The XRD patterns for the non-irradiated and irradiated samples show well-defined peaks of which could be indexed on the basis of the Bi-2212 phase structure. XRD patterns also indicate that irradiation did not affect the Bi-2212 superconducting phase. However, the enhancement of Jc was observed in the neutron irradiated sample and this indicates the effectiveness of .neutron irradiation in creating defects that acted as effective flux pinning centers for vortices.
Publisher
Trans Tech Publications, Ltd.
Subject
Condensed Matter Physics,General Materials Science,Atomic and Molecular Physics, and Optics
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献
1. Crystal chemistry and electrical properties of La-doped BaTiO3;PROCEEDINGS OF 8TH INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS ENGINEERING & TECHNOLOGY (ICAMET 2020);2021