Network Carbide Inheritance during Heat Treatment Process of Large Shield Machine Bearing Steel GCr15SiMn

Abstract

Network carbide inheritance during heat treatment process of large shield machine bearing steel GCr15SiMn was investigated by heat treatment experiments and quantitative metallographic. Samples with the proeutectoid cementite network thickness in the range of 0.19~0.54 μm were obtained by changing austenitizing temperature and soaking time of pearlite transformation. The results show that the network in hot rolled bar can be improved when the pre-heat treatment temperature is 950 °C. When the network thickness is above 0.40 μm, the undissolved cementite networks present in microstructures after quenching and tempering. In a Chinese standard, the network grades are 1.5 and 3.0 degree when the networks thickness are 0.40 μm and 0.54 μm, respectively. The critical network thickness that can be eliminated by heat treatment is 0.29 μm.