In the present work, 2% and 6% carbon nanotubes (CNT) were reinforced in chromium oxide powder and were deposited on T22 steel using high velocity oxy-fuel spraying process. The effect of CNT reinforcement on hardness and porosity was investigated. The hardness was observed to be highest for coating reinforced with 6%CNT and hardness was found to increase with decrease in porosity. The coating microstructure and elements were characterised using field emission scanning electron microscopy (FE-SEM) with energy dispersive spectroscope (EDS), Elemental point analysis and X-ray mapping analysis. The constituents of the coating were identified using X-ray diffractometer. It was found that the CNT were uniformly distributed throughout Cr2O3matrix. The CNT were found to be chemically inert during the spraying process.
Publisher
Trans Tech Publications, Ltd.
Reference34 articles.
1. C. A. Duarte, E. Espejo, and J. C. Martinez, Failure analysis of the wall tubes of a water-tube boiler,, Engineering Failure Analysis, Vol. 79, pp.704-713, (2017).
2. Q. Ding, X.-F. Tang, and Z.-G. Yang, Failure analysis on abnormal corrosion of economizer tubes in a waste heat boiler,, Engineering Failure Analysis, Vol. 73, pp.129-138, (2017).
3. M. Loghman-Estarki, R. S. Razavi, H. Edris, S. Bakhshi, M. Nejati, and H. Jamali, Comparison of hot corrosion behavior of nanostructured ScYSZ and YSZ thermal barrier coatings,, Ceramics international, Vol. 42, No. 6, pp.7432-7439, (2016).
4. K. Goyal, H. Singh, and R. Bhatia, Current Status of Thermal Spray Coatings for High Temperature Corrosion Resistance of Boiler Steel,, Journal of Material & Metallurgical Engineering, Vol. 6, No. 1, pp.29-35, (2016).
5. V. P. S. Sidhu, K. Goyal, and R. Goyal, Comparative study of corrosion behaviour of HVOF-coated boiler steel in actual boiler environment of a thermal power plant,, Journal of the Australian Ceramic Society, pp.1-8, (2017).
Cited by
14 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献