Initiation and Growth of Pits and Cracks in Corrosion Fatigue for High Strength Aluminium Alloy Observed by Micro Computed-Tomography Using Ultra-Bright Synchrotron Radiation-Reference-Cited by-同舟云学术

Initiation and Growth of Pits and Cracks in Corrosion Fatigue for High Strength Aluminium Alloy Observed by Micro Computed-Tomography Using Ultra-Bright Synchrotron Radiation

Published:2011-07 Issue: Volume:83 Page:162-167
ISSN:1662-7482
Container-title:Applied Mechanics and Materials
language:
Short-container-title:AMM

Author:

Nakai Yoshikazu¹,Shiozawa Daiki¹

Affiliation:

1. Kobe University

Abstract

Measurement of shape and dimension of pits and cracks formed in corrosion fatigue tests of a high-strength aluminium alloy, 7075-T651 were conducted by computed-tomography using ultra bright synchrotron radiation X-ray. Complex corrosion process could be observed and detail shapes of corrosion pits could be identified. Sometimes, corrosion pit and corroded area were formed under passive film, and those were not observed from the surface.

Publisher

Trans Tech Publications, Ltd.

Link

https://www.scientific.net/AMM.83.162.pdf

Reference9 articles.

1. K. Komai, J. Kikuchi, Stereo Fractography, Yokendo (Tokyo, 1996), p.48.

2. K. Komai, K. Minoshima, M. Itoh, J. Soc. Mat. Sci., Japan, 43 (1994), p.336.

3. Y. Nakai, S. Fujiwara, T. Ogawa, Y. Shimizu, Mat. Sci. Res. Int., STP1 (2001), p.101.

4. Y. Nakai, Y. Shimizu, S. Fujiwara, T. Ogawa, Proc. 10th Int. Conf. on Fracture, CD-ROM, (2001), p.101.

5. R. P. Wei, D. G. Harlow, Proc. Fatigue 99 (1999), p.2197.

Cited by 7 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Change of misorientation of individual grains in fatigue of polycrystalline alloys by diffraction contrast tomography using ultrabright synchrotron radiation;Procedia Structural Integrity;2017

2. 4D evaluation of grain shape and fatigue damage of individual grains in polycrystalline alloys by diffraction contrast tomography using ultrabright synchrotron radiation;International Journal of Fatigue;2016-01

3. Real-Time Monitoring of Aluminum Crevice Corrosion and Its Inhibition by Vanadates with Multiple Beam Interferometry in a Surface Forces Apparatus;Journal of The Electrochemical Society;2015

4. Evaluation of Fatigue Damage by Diffraction Contrast Tomography Using Synchrotron Radiation;Materials Science Forum;2014-05-23

5. Evaluation of Fatigue Damage by Diffraction Contrast Tomography Using Synchrotron Radiation;Advanced Materials Research;2014-03