Preparation of (Ba1-x, Srx)TiO3 Thin Films on Glazed Alumina Substrate and Improvement of Temperature Dependence of Dielectric Properties

Author:

Nozaka Takashi1,Mizutani Yoji1,Bhakdisongkhram Gun1,Kawakami Yuta2,Echizen Masahiro2,Nishida Takashi2,Takeda Hiroaki3,Uchiyama Kiyoshi2,Shiosaki Tadashi2

Affiliation:

1. Yokohama Densi Seiko Co., Ltd.

2. Nara Institute of Science and Technology

3. Tokyo Institute of Technology

Abstract

In this study, (Ba1-x,Srx)TiO3 thin films of various composition ratios were deposited on glazed Al2O3 substrates by the CSD method, and the temperature dependence of the dielectric property was analyzed. The dielectric property of the BST (80/20) thin film annealed at C was highly tunable, and the temperature dependence of the dielectric constant was stabilized at around room temperature. However, this BST (80/20) thin film exhibited intense ferroelectricity. Its tan intensified to 0.0511 in the high-frequency range (1 MHz). After the BST thin film was annealed at 600C, the grain size of the BST thin film was reduced to 40 nm and the ferroelectricity was alleviated. The dielectric constant, tan, and tunability of the BST thin film at 100 kHz were 158, 0.0170, and 39.6 (214 kV/cm, 6.0 V), respectively. The change rate of the dielectric constant, which indicates its temperature dependence, was ±7 or less in the range of -55 to 85C. Therefore, this BST thin film was considered to guarantee a wide operation temperature range for microwave tunable devices.

Publisher

Trans Tech Publications, Ltd.

Subject

Mechanical Engineering,Mechanics of Materials,General Materials Science

Cited by 1 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3