Affiliation:
1. Panasonic Electronic Devices Co., Ltd.
Abstract
BaTiO3 powders with particle size 0.1μm were made by solid state synthesis. To make high tetragonality BaTiO3 powder, mixture of TiO2 and BaCO3 was calcined in vacuum condition. And to make low tetragonality BaTiO3 powder, the mixture was calcined in air condition. With each powder, MLCCs with Ni-internal electrode were fabricated. Relationships between temperature and relative dielectric constant of MLCCs’ dielectric layers were analyzed and their dielectric grains were observed by TEM-EDS. As the result, MLCC made from high tetragonality BaTiO3 powder had good temperature characteristics and core-shell dielectric grains.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference5 articles.
1. K. Tokita and S. Sato, Key Engineering Materials, 320 (2006) p.143.
2. Y. Sakabe, I. Nakamura and N. Wada, Ceramic Processing Science VI, (2001) p.3.
3. Y. Fujikawa, Y. Umeda and F. Yamane, J. Jpn. Soc. Powder Powder Metallurgy, 51(12) (2004) p.839.
4. H. Saito, H. Chazono, H. Kishi and N. Yamaoka, Jpn. J. Appl. Phys., 30 (1991) p.2307.
5. D. Hennings and G. Rosenstein, J. Am. Ceram. Soc., 67 (1984) p.249.