Abstract
Perovskite SrZrO3 ceramics were successfully prepared via a combustion technique. The effect of calcination temperatures (900-1400oC) and sintering temperatures (1400-1650oC) on phase and morphology evolution of perovskite SrZrO3 ceramics were studied. The highest purity of perovskite phase powder was obtained at 1250 oC and the purity of the perovskite phase of SrZrO3 ceramics were detected in the samples sintered at 1550 oC for 6 h. The SEM results showed the average particle size (84-214 nm) and the average grain size (0.35-2.09 µm) of samples increased with the increase of firing temperatures. The shrinkage of the ceramics increased as the sintering temperatures increased. The maximum density was ~98.4% of the theoretical density for the sample sintered at 1550 oC for 6 h.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference14 articles.
1. E. A. Slonimskaya and A. V. Belyakov, Glass Ceram., 58 (2001), p.54.
2. T. Yajima, H. Suzuki, T. Yoyo and H. Iwahara, Solid State Ion., 51 (1992), p.101.
3. T. Osaka, C. Numako and K. koto, Res. Bull., 34 (1999), p.11.
4. E. K. Keler and A. K. Kuzestor, Zh. Prikl Khim, 34 (1961), p.2146.
5. M. Rajendran and M. Subba Rao, J. Mater. Res., 12 (1997), p.2665.
Cited by
17 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献