A Nb-Ti-Mo high strength steel was selected at two different cooling rates through ultra-fast cooling process, and its microstructures and strengthening mechanisms were analyzed. The results show the size of ferrite was decreased and the amount of bainite and micro-hardness were increased with increasing of cooling rate through thermal simulation. The UFC technology can improve the yield and tensile strength 25MPa and 35MPa, respectively, compared with conventional TMCP. The microstructure of this steel is mainly ferrite and good strength and toughness are caused by the refinement of ferrite and fine precipitates. Ultra-fast cooling technology improves the strength and toughness of this steel effectively.
Publisher
Trans Tech Publications, Ltd.
Reference5 articles.
1. Guo Dong Wang, Sheng-jie Yao: Angang technology (2009), p.1.
2. Guo Dong Wang: Journal of Northeastern University (Natural Science) (2009), p.913.
3. Yi Hai Long, Liu Zhen Yu, Wang Guo Dong, Wu Di: Journal of Iron and Steel Research, International Vol. 17(2010), p.54.
4. Guo Dong Wang: Shanghai Metals Vol. 3 (2008), p.1.
5. J.C. Herman, B. Donnay: ISIJ International Vol. 32 (1992), p.779.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献