Magnesium Phosphate Cement with Large Volume of Fly Ash

Abstract

The accumulation of fly ash leads to severe problems in ecological environments. Various ways to excite the activity of fly ash in Portland cement based cementitious materials have been carried out for many years. In the present study, effect of large volume of fly ash in phosphate cement was studied. Dead burned magnesia, two phosphates (monoammonium phosphate and monosodium phosphate), and fly ash were used. The fabricated cement mortar specimens with different fly ash dosages were cured for 28 days in the lab air. Compressive strength was determined in 1d, 3d, 7d and 28d respectively. It is showed the compressive strength reduced with increase of fly ash content and increased with the curing time. After cured 28 days, the compressive strength of cement mortar developed to14MPa, when 80% fly ash was used. The reaction product, Na2HPO4•17H2O was found by X-ray diffraction analysis in sodium phosphate based cement. No ammonia gas was emitted and large volume of fly ash can be used in cement prepared from sodium phosphate. It is a new environmentally friendly cement material.