Abstract
Microstructural evolution of bulk undercooled Ni-40wt%Pb hypermonotectic alloy was systematically investigated by using molten glass purification and superheating cycling. Within the achieved undercooling range, the microstructures were classified into three categories. When the undercooling was less than 50K, the microstructure consisted of coarse dendritic grain and interdendritic Pb lumps. Increasing undercooling to the range 100 to 198K, macrosegregation was serious. When the undercooling was up to 292K, refined granular grain with homogeneously distributed fine Pb particles on it formed. The granulation mechanism of granular grains was owing to dendritic disintegration and subsequent recrystallization.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference13 articles.
1. P. Nash: PDBNA (Materials Park, OH 44073, 1991), p.247.
2. B. Predel: JPE, Vol. 18, (1997), p.327.
3. Z. B Dwyer: Diss. Abstr. Int. Univ. Alabama (Birmingham), USA, Vol. 55, (1995), p.179.
4. I. Aoi, M. Ishno, M. Yoshida, H. Fukunaga and H. Nakae: J. Cryst. Growth Vol. 222 (2001), P. 806.
5. H. Fujii, T. Kimura, H. Kitaguchi, et al.: J. Mater. Sci. Vol. 30 (1995), p.3429.
Cited by
11 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献