Rolling and Recrystallization Textures in High Purity Al Cold Rolled to Very High Rolling Reductions

Author:

Todayama Atsushi1,Inagaki Hirosuke1

Affiliation:

1. Shonan Institute of Technology

Abstract

On the basis of Taylor-Bishop-Hill’s theory, many previous theoretical investigations have predicted that, at high rolling reductions, most of orientations should rotate along theβfiber from {110}<112> to {123}<634> and finally into the {112}<111> stable end orientations. Although some exceptions exist, experimental observations have shown, on the other hand, that the maximum on the β fiber is located still at about {123}<634> even after 97 % cold rolling. In the present paper, high purity Al containing 50 ppm Cu was cold rolled up to 99.4 % reduction in thickness and examined whether {112}<111> stable end orientation could be achieved experimentally. It was found that, with increasing rolling reduction above 98 %, {110}<112> decreased, while orientations in the range between {123}<634> and {112}<111> increased, suggesting that crystal rotation along the βfiber from {110}<112> toward {123}<634> and {112}<111> in fact took place. At higher rolling reductions, however, further rotation of this peak toward {112}<111> was extremely sluggish, and even at the highest rolling reduction, it could not arrive at {112}<111>. Such discrepancies between theoretical predictions and experimental observations should be ascribed to the development of dislocation substructures, which were formed by concurrent work hardening and dynamic recovery. Since such development of dislocation substructures are not taken into account in Taylor-Bishop-Hill’s theory, it seems that they can not correctly predict the development of rolling textures at very high rolling reductions, i. e. stable end orientations. On annealing specimens rolled above 98 % reduction in thickness, cube textures were very weak, suggesting that cube bands were almost completely rotated into other orientations during cold rolling. {325}<496>, which lay at an intermediate position between {123}<634> and {112}<111> along theβfiber, developed strongly in the recrystallization textures.

Publisher

Trans Tech Publications, Ltd.

Subject

Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science

Reference14 articles.

1. W. Norman: Z. Metallkd. Vol. 55 (1964), p.347.

2. A. Korbel, J. D. Embury, H. Hartherley, P. L. Marin and H. W. Erbsloh: Acta metall. Vol. 34 (1986), p. (1999).

3. J. Hirsch and K. Lücke: Acta metall. 36 (1988), p.2883.

4. K. Lücke and O. Engler: Mater. Sci. Technl.: Vol. 6 (1990), p.1113.

5. P. Wagner, O. Engler and K. Lücke: Textures and Microstructures Vol. 14-18 (1991), p.297.

Cited by 8 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3