The interface morphologies single crystal superalloys CMSX-2 has been studied over a range of cooling rate with large variations in withdrawal speed in directional solidification. The superfine cellular structure was obtained under both high thermal gradient up to 1000K/cm and fast withdrawal rate up to 1mm/sec. The high rate directional solidification results in reduction in primary and secondary dendrite arm spacing, refinement of λ’ phase, reduced microsegregation of alloying elements and smaller size of γ-γ’ eutectics.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference10 articles.
1. M. Konter, and M. Thumann: Journal of Materials Processing Technology, 2001, 117, 386.
2. L. Lohmueller, W. Esser, J. Grossmann, M. Hoerdler, J. Preuhs, R. F. Singer: in Superalloy 2000, TMS, Warrendale, PA, 2000, 181.
3. M. Konter, E. Kats, N. Hofmann: in Superalloy 2000, TMS, 2000, 189.
4. D. Ma, and U. Grafe: Materials Science and Engineering, 1999, A270, 339.
5. A. Kermanpur, N. Varahraam, E. Engilehei, M. Mohammadzadeh, and P. Davami: Materials Science and Technology, 2000, 16, 579.
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献