Affiliation:
1. Jiangsu University of Science and Technology
Abstract
This paper prepared Cu-ZrO2 composite by a modified internal oxidation in order to improve the high temperature strength of resistance Spot-welding electrode. The results showed that with the increasing of the cold deformation, Hardness increased while electrical conductivity decreases. Hardness reached 100HV and electrical conductivity was up to 86%IACS after cold drawn in 56%. With the increasing of annealing temperature and annealing time, Hardness of the composite decreased more slowly compared with the conventional Cu-Cr-Zr alloy and was higher than that of the Cu-Cr-Zr alloy after annealed above 700°C for 2h and at 600°C for 5h , which was attributed to the dispersion strengthening effect of the Zirconia particles. Thus, the Cu-ZrO2 composite has good high-temperature stability and can be used for the electrode
Publisher
Trans Tech Publications, Ltd.
Reference11 articles.
1. Nied H. A, US Patent 4, 514, 612; (1985).
2. Xu Mei, Jian Li, Shijie Dong, Hot Working Technology, 2003(4): 46-48. In Chinese.
3. Moustafa SF, Abdel-Hlhay AM. Mater Lett 2002; 53: 244-9.
4. JinXue Li, Rui Hu, JinShan Li, Power Metallurgy Technology, 2002, 20(5): 276-279. In Chinese.
5. Baohong Tian, Ping Liu, Kexing Song. Material Science and Engineering (2006), 705-710.
Cited by
6 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献