Affiliation:
1. Jilin University
2. First Automobile Works Foundry Co. Ltd
Abstract
Microstructures and properties of plasma surfaced NiCrBSi+20%WC/12Co layer prepared on the die steel (H13) substrate were investigated. The study showed that the interface boundary existed between the layer and substrate. Compared with the typical microstructures of welded joint, the similar columnar grains in the layer perpendicular to the interface line were observed, which were never seen in the plasma sprayed coating. The conclusion could be drawn that the bonding between the NiCrBSi+20%WC/12Co layer and H13 substrate belonged to the metallurgical cohesion. The XRD analysis showed that the main phases in the layer included γ-(Fe, Ni), Cr7BC4, Ni4B3, Cr7C3 and Co7W6, which brought higher strength and higher hardness to the surfaced layer than the H13 substrate.
Publisher
Trans Tech Publications, Ltd.
Reference8 articles.
1. T. Ahmet and B. Cuma: Materials and Manufacturing Processes, Vol. 24(2009), P. 898-902.
2. C.G. Pan, H.C. Wang and J.L. Zhou: 2010 International Conference on Computing, Control and Industrial Engineering, Vol. 2(2010), P. 12-15.
3. V.V. Ivanov, I.R. Paine and P.J. Revnyuk: High Temperature Materials and Processes, Vol. 21(2002), P. 65-78.
4. T. Muhic, J. Tusek, M. Pleterski and D. Bombac: Metalurgija, Vol. 48(2009), P. 39-42.
5. X.Q. Bi, X. L. Hu and J. Wang: Journal of Aeronautical Materials, Vol. 29(2009), P. 45-49. (In Chinese).
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献