Using tetraethoxysilane (TEOS) and novolac-PF as raw materials, SiO2/PF hybrid fibers were prepared via sol-gel associated with drawing process, and then sintered at different temperatures (500-1300 °C) under air atmosphere. The microstructure variation and reaction mechanism of the fiber were investigated by FT-IR, XRD, and SEM measurements. The results showed that the microstructure variation of the hybrid fiber was influenced greatly by sintering temperatures. When the sintering temperature was below 900 °C, the fibers were amorphous, and converted into porous SiO2/SiC fibers after being sintered at 1300 °C.
Publisher
Trans Tech Publications, Ltd.
Reference20 articles.
1. T. Tezuka, K. Tadanaga, A. Hayashi, M. Tatsumisago, Solid. State. Ionics. 179 (2008), p.1151.
2. J. Tronto, F. Leroux, M. Dubois, C. Taviot-Gueho. J.B. Valim, J. Phys. Chem. Solids. 67 (2006), p.978.
3. R.D. Maggio, S. Dirè, E. Callone, F. Girardi, G. Kickelbick, J. Sol-Gel. Sci. Tech. 48 (2008), p.168.
4. K. Iketani, R.D. Sun, M. Toki, K. Hirota, O. Yamaguchi, J. Phys. Chem. Solids. 64 (2003), p.507.
5. Q.S. Song, T.J. Shi, H.H. Ma, Polym. Bull. 61 (2008), p.473.