Preparing and Sphericizing Ultrafine Graphite Particles with Stirred Mill

Published:2014-07 Issue: Volume:539 Page:785-789
ISSN:1662-7482
Container-title:Applied Mechanics and Materials
language:
Short-container-title:AMM

Author:

Zhang Ling Yan¹,Qiu Yang Shuai¹,Hong Wei¹,Deng Cheng Cai¹

Affiliation:

1. Wuhan University of Technology

Abstract

The ultrafine graphite particles was prepared and sphericized by stirred mill. By the conditional tests, the influences of the main operation parameters, such as ball-to-powder weight ratio, grinding concentration, dispersant dosage, agitator speed on grinding efficiencies of stirred mill were studied systematically .The reasons of the influence was analyzed. The study results offered suitable operation parameters for practical production. The scanning electron microscope (SEM) was employed to investigate the structure of the ore sample. The result showed the sphericity of product was improved than the raw material.

Publisher

Trans Tech Publications, Ltd.

Link

https://www.scientific.net/AMM.539.785.pdf

Reference12 articles.

1. Yue-Zhao CUI, Pei-Kang RONG，Shao-Hua ZHANG, et al. Non-metallic Industry of China [ M]. Beijing: Geological Press, (2008).

2. Feng-Sheng LI. Ultrafine Powder Technology [M]. Beijing: National Defense Industry Press.

3. Guo-Wang ZHANG, Shen-Sheng HUANG, et al. Application of ultrafine powder preparation technology and its development [J]. Chemical Minerals and Process, 2001( 12) : 1- 3.

4. Hua-Ming YANG, 1998. Study on the superfine comminution and mechanochemistry by agitating grinding mill, PhD Thesis, Central South University, China.

5. B. G. Kim, S .K. Choi, H. S. Chung, et al. Grinding characteristics of crystalline graphite in a low - pressure at trition system [J]. Powder Technology, 2002(126): 22- 27.