Abstract
Silane treatment has been applied as a chromium free multi-metal surface treatment for its characteristics of corrosion protection, adhesion promotion and metal surface passivation. Vinyltriethoxysilane(VTES) hydrolysis solutions with the concentration of 4% and 10% were prepared, respectively. Morphologies and microstructures of the VTES films both before and after the corrosion test were observed with a scanning electron microscope (SEM), and effect of cure temperature on the corrosion resistance of silane film was studied combined with electrochemical impedance spectroscopy (EIS). The results showed that the cure temperature affects condensation states of silanol groups –Si–OH in silane films and promotes the forming of –Si–O–Si– network structure, and as a consequence influences the corrosion resistance of VTES films.
Publisher
Trans Tech Publications, Ltd.
Reference15 articles.
1. M. Schneider, M.M. Lohrengel, C. Rosenkranz, A. Schreiber, E. Kock, M. Beneke, in: Proceedings of the 3rd International Symposium on Aluminium Surface Science and Technology, Bonn, Germany, (2003), p.247.
2. R. Zandi-zand, A. Ershad-langroudi, A. Rahimi, Prog. Org. Coat. Vol. 53 (2005), p.286.
3. V. Subramanian, W.J. van Ooij, Surf. Eng. Vol. 15 (1999), p.168.
4. M.F. Montemor, A.M. Simoes, M.G.S. Ferreira, B. Williams, H. Edwards, Prog. Org. Coat. Vol. 38 (2000), p.17.
5. D. Zhu, W.J. van Ooij, Prog. Org. Coat. Vol. 49 (2004), p.42.
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献