Study on the β1→α+β2 Transformation Kinetics of Ti-6Al-4V Alloy by DSC-Reference-Cited by-同舟云学术

Study on the β1→α+β2 Transformation Kinetics of Ti-6Al-4V Alloy by DSC

Published:2014-01 Issue: Volume:508 Page:110-113
ISSN:1662-7482
Container-title:Applied Mechanics and Materials
language:
Short-container-title:AMM

Author:

Zhang Rong Hua¹,Wu Biao²,Zheng Xiao Ping²

Affiliation:

1. Hebei United University

2. National Engineering Research Center of Near-Net-Shape Forming for Metallic Materials

Abstract

The temperature and duration of β1→α+β2 transformation of Ti-6Al-4V alloy in cooling process were measured by differential scanning calorimetry, and transformation activation energy and Avrami exponent of β1→α+β2 were also calculated. The results show that the cooling rate is in the range of 在5～20°C/min, the transformation temperature and the transformation duration β1→α+β2 transformation of Ti-6Al-4V alloy decreased with the increasing cooling rate, its transformation activation energy decreased with the increasing phase transformation volume fraction, and Avrami exponent was between 1 and 2 at 660°C.

Publisher

Trans Tech Publications, Ltd.

Link

https://www.scientific.net/AMM.508.110.pdf

Reference9 articles.

1. Sun L P, Lin G Y, Liu J, et al. Effect of low temperature thermo-mechanical treatment on microstructures and mechanical properties of TC4 alloy [J]. Journal of Central South University of Technology (English Edition), 2010, 17(3): 443-448.

2. Sun S D, Zong Y Y, Shan D B, et al. Hot deformation behavior and microstructure evolution of TC4 titanium alloy [J]. Transactions of Nonferrous Metals Society of China, 2010, 20(11): 2181-2184.

3. Niinomi M. Recent research and development in titanium alloys for biomedical applications and healthcare goods[J]. Science and Technology of Advanced Materials, 2003(4): 45-454.

4. Miller R M, Bieler T R, Semiatin S L. Flow softening during hot working of Ti-6Al-4V with a lamellar colony microstructure[J]. Scripta Mater, 1999, 40(12): 1387-1393.

5. Dong H B, Yang X. Heat-treated microstructure and mechanical properties of TC4 alloy [J]. Advanced Materials Research, 2011, ( 197-198): 1524-1527.